Saves OLD ZINC DIE CAST SCRAP
Shall consist of miscellaneous old zinc base die castings,
with or without iron and other foreign attachments.
Must be free of borings, turnings, dross
pieces, chunks, melted pieces and skimmings. All
unmeltables, dirt, foreign attachments, and volatile
substances (such as rubber, cork, plastic, grease,
etc.) are deductible. Material containing in excess of
30% iron will not constitute good delivery.
Scabs NEW ZINC DIE CAST SCRAP
Shall consist of new or unused, clean, zinc base die
castings. Castings to be unplated, unpainted, and
free from corrosion.
Scoot ZINC DIE CAST AUTOMOTIVE GRILLES
Shall consist of clean, old or used zinc base die cast
automotive grilles, free from soldered material. All
foreign attachments and extraneous materials are
deductible.
Scope NEW PLATED ZINC DIE CAST SCRAP
Shall consist of new or unused clean, plated zinc
base die castings, free from corrosion.
Score OLD SCRAP ZINC
Shall consist of clean dry scrap zinc, such as sheets,
jar lids, clean unalloyed castings and anti-corrosion
plates. Borings and turnings are not acceptable.
Material must not be excessively corroded or oxidized.
All foreign attachments and extraneous materials
are deductible.
Screen NEW ZINC CLIPPINGS
Shall consist of any new pure zinc sheets or stampings
free from corrosion. To contain no foreign material
or attachments. Printers zinc, such as engravers
zinc, lithograph sheets and addressograph plates
subject to special arrangements. Printers zinc to be
free of routings.
Scribe CRUSHED CLEAN SORTED FRAGMENTIZERS DIE CAST SCRAP,AS PRODUCED FROM AUTOMOBILE FRAGMENTIZERS
To be clean, free of dirt, oil, glass, rubber, and trash.
To contain a maximum of 5% unmeltables such as
free iron, copper, aluminum and other metals.
Scroll UNSORTED ZINC DIE CAST SCRAP
Produced from automobile fragmentizers. Material
to contain about 55% zinc-bearing scrap. Other
nonferrous metals such as aluminum, stainless steel,
red metal, etc., to be about 40%. Insulated copper
wire about 1%. Trash, dirt, glass, rubber, oil, iron, not
to exceed 5%. Any variations to be sold by special
arrangement between buyer and seller.
Scrub HOT DIP GALVANIZERS SLAB ZINC DROSS (Batch Process)
Shall consist only of galvanizers unsweated zinc
dross in slab form from hot dip galvanizing (Batch
Process) with a minimum zinc content of 92% and
shall be free of skimmings and tramp iron. Broken
pieces under 2” in diameter shall not exceed 10% of
the weight of each shipment. Slabs shall not weigh
over 100 pounds each. Heavier pieces acceptable
upon mutual agreement between buyer and seller.
Material from continuous galvanizing operation is
not acceptable. Blocks are acceptable upon mutual
agreement.
Scull ZINC DIE CAST SLABS OR PIGS
Shall consist of melted zinc base die cast materials,
in smooth clean solid slabs or pigs. Material to be
free from drosses and to contain a minimum zinc
content of 90%. To contain a maximum of 0.1%
nickel and maximum of 1% lead. Blocks are acceptable
upon mutual agreement.
Seal CONTINUOUS LINE GALVANIZING SLAB ZINC TOP DROSS
Shall consist of unsweated zinc dross removed from
the top of a continuous line galvanizing bath, in slab
form not weighing in excess of 100 pounds each,
with a minimum zinc content of 90%. Heavier pieces
acceptable upon mutual agreement between buyer
and seller. Shall be free of skimmings. Broken pieces
under 2” in diameter shall not exceed 10% of the
weight of each shipment.
Seam CONTINUOUS LINE GALVANIZING SLAB ZINC BOTTOM DROSS
Shall consist of unsweated zinc dross removed from
the bottom of a continuous line galvanizing bath, in
slab form not weighing in excess of 100 pounds each,
with a minimum zinc content of 92%. Heavier pieces
acceptable upon mutual agreement between buyer
and seller. Shall be free of skimmings. Broken pieces
under 2” in diameter shall not exceed 10% of the
weight of each shipment.
Shelf PRIME ZINC DIE CAST DROSS
Shall consist of metal skimmed from the top of pot
of molten zinc die cast metal. Must be unsweated,
unfluxed, shiny, smooth, metallic and free from corrosion
or oxidation. Should be poured in molds or in
small mounds weighing not over 75 pounds each.
Zinc content shall be minimum of 85%.